Military grade heat shrink marker sleeve is developed environment-friendly flame retardant heat shrinkable tube,
using specially designed formulation of high polymers, through cross-link by electronic accelerator and continuous expansion.
Heat Shrink Identification Tubing are designed to meet the wire and cable marking needs of manufacturers with high performance requirements. Made from permanent, flame retarded, radiation cross-linked heat-shrinkable polyolefin.
| Material | The sleeving shall be fabricated from irradiated, thermally stabilized and flame retarded modified PVDF |
|---|---|
| Application range | Aerospace, defense and mass transit industries. |
| Operating temperature range | -55~+225℃ |
| Minimum recovery temperature | +150 ℃ |
| Maximum storage temperature | +50 ℃ |
| Shrink ratio | 2:1 |
| Color | White, Yellow, other color is available if ordered |
| Printing mode | Single sided printing and Double sided printing formats available |
| Supplied mode | Either Continuous type or Ladder format type is available |
| Recommended Printers | Thermal transfer printer |
| Recommended Ribbons | N95 resin ribbon, Black, 100mm(width)*300m(length) |
| Property | Unit | Requirement | Test Method |
| Size | mm | As supplied | ASTM D 2671 |
| Longitudinal Change | % | -10~+5 | ASTM D 2671 |
| Tensile Strength | MPa | ≥24.1 | ASTM D 2671 |
| Ultimate Elongation | % | ≥300 | ASTM D 2671 |
| Specific Gravity | g/cm3 | ≤1.9 | ASTM D 2671 |
| Low Temperature Flexibility（ -55℃ 、 4h ） | — | No Cracks | AMS-DTL-23053 |
| Heat Shock （ 275 ℃ 、 4h ） | — | No cracking, flowing or dripping | ASTM D 2671 |
| Tensile Strength after Heat Aging （ 225℃ 、 168h ） | MPa | ≥19.1 | ASTM D 2671 |
| Ultimate Elongation after Heat Aging （ 225℃ 、 168h ） | % | ≥200 | ASTM D 2671 |
| Dielectric Strength | Kv/mm | ≥15.7 | ASTM D 2671 |
| Volume Resistivity | Ω·cm | ≥1012 | ASTM D 2671 |
| Corrosive Effect （ 160℃ 、 16h ） | — | No corrosion | ASTM D 2671 |
| Flammability | — | Pass | UL224 VW-1， ASTM D 2671 |
| Water Absorption （ 23℃ 、 24h ） | % | ≤0.5 | ISO 846 Procedure B |
| Print Permanence | — | Print legible after 50 rubs | SAE AS81531 |
| Print Permanence after Heat Aging （ 225℃ 、 168h ） | — | Print legible after 50 rubs | SAE AS81531 |
| Print Permanence after Fluid Resistance | — | Print legible after 50 rubs | MIL-STD-202F, method 215J |
Military grade heat shrink marker sleeve is developed environment-friendly flame retardant heat shrinkable tube,
using specially designed formulation of high polymers, through cross-link by electronic accelerator and continuous expansion.
Heat Shrink Identification Tubing are designed to meet the wire and cable marking needs of manufacturers with high performance requirements. Made from permanent, flame retarded, radiation cross-linked heat-shrinkable polyolefin.
| Material | The sleeving shall be fabricated from irradiated, thermally stabilized and flame retarded modified PVDF |
|---|---|
| Application range | Aerospace, defense and mass transit industries. |
| Operating temperature range | -55~+225℃ |
| Minimum recovery temperature | +150 ℃ |
| Maximum storage temperature | +50 ℃ |
| Shrink ratio | 2:1 |
| Color | White, Yellow, other color is available if ordered |
| Printing mode | Single sided printing and Double sided printing formats available |
| Supplied mode | Either Continuous type or Ladder format type is available |
| Recommended Printers | Thermal transfer printer |
| Recommended Ribbons | N95 resin ribbon, Black, 100mm(width)*300m(length) |
| Property | Unit | Requirement | Test Method |
| Size | mm | As supplied | ASTM D 2671 |
| Longitudinal Change | % | -10~+5 | ASTM D 2671 |
| Tensile Strength | MPa | ≥24.1 | ASTM D 2671 |
| Ultimate Elongation | % | ≥300 | ASTM D 2671 |
| Specific Gravity | g/cm3 | ≤1.9 | ASTM D 2671 |
| Low Temperature Flexibility（ -55℃ 、 4h ） | — | No Cracks | AMS-DTL-23053 |
| Heat Shock （ 275 ℃ 、 4h ） | — | No cracking, flowing or dripping | ASTM D 2671 |
| Tensile Strength after Heat Aging （ 225℃ 、 168h ） | MPa | ≥19.1 | ASTM D 2671 |
| Ultimate Elongation after Heat Aging （ 225℃ 、 168h ） | % | ≥200 | ASTM D 2671 |
| Dielectric Strength | Kv/mm | ≥15.7 | ASTM D 2671 |
| Volume Resistivity | Ω·cm | ≥1012 | ASTM D 2671 |
| Corrosive Effect （ 160℃ 、 16h ） | — | No corrosion | ASTM D 2671 |
| Flammability | — | Pass | UL224 VW-1， ASTM D 2671 |
| Water Absorption （ 23℃ 、 24h ） | % | ≤0.5 | ISO 846 Procedure B |
| Print Permanence | — | Print legible after 50 rubs | SAE AS81531 |
| Print Permanence after Heat Aging （ 225℃ 、 168h ） | — | Print legible after 50 rubs | SAE AS81531 |
| Print Permanence after Fluid Resistance | — | Print legible after 50 rubs | MIL-STD-202F, method 215J |